R1 Wraparound Heat Shrinkable Cable Repair Sleeve with heat reactive paint
| R1 Wraparound Heat Shrinkable Cable Repair Sleeve |
| Features |
| Semi-rigid out layer, adhesive lined,moisture-proof |
Operating temperature: -25~90ºC |
| Emergency cable repair and sealing system |
Shrink temperature: 135ºC |
| Abrasion and corrosion resistant |
Halogen free |
| Steel channel enables permanent closure system |
RoHS compliant |
| Quickly fitted in breakage,insulating and air-tight repair |
| Technical Data |
| Property |
Test method |
Values |
| Physical |
Tensile strength |
ASTM D2671 |
≥14 MPa |
| |
Breakdown elongation |
ASTM D2671 |
≥ 350% |
| Aging (150ºC /168hrs) |
Tensile strength |
ASTM D2671 |
≥12 MPa |
| Breakdown elongation |
ASTM D2671 |
≥300% |
| |
Density |
ASTM D792 |
1.1~1.2 |
| |
Low temperature flexibility(-25 ºC/4hrs) |
ASTM D2671 |
No cracking |
| |
Hardness (Shore D) |
ASTM D2240 |
40~50 HD |
| |
Heat shock (200 ºC/4hrs) |
ASTM D2671 |
No cracking ,no flow |
| |
Water absorption |
ASTM D570 |
≤0.5% |
| Electrical |
Volume resistivity |
ASTM D257 |
≥1013 Ω.cm |
| |
Dielectric strength |
ASTM D2671 |
15 KV/mm |
| |
Dielectric constant |
IEC 250 |
≤ 5.0 |
| Chemical |
Fungus resistance |
ASTM G21 |
No growth |
| Dimensions |
| Reference |
As supplied |
After recovered |
Standard length |
| UPM R1 |
(mm) |
(mm) |
m |
| R1-36/10 |
36 |
10 |
1 |
| R1-50/15 |
50 |
15 |
1 |
| R1-60/18 |
60 |
18 |
1 |
| R1-70/22 |
70 |
22 |
1 |
| R1-80/25 |
80 |
25 |
1 |
| R1-100/30 |
100 |
30 |
1 |
| R1-135/38 |
135 |
38 |
1 |
| R1-164/42 |
164 |
42 |
1 |
| R1-185/55 |
185 |
55 |
1 |
| R1-200/60 |
200 |
60 |
1 |
| R1-220/65 |
220 |
65 |
1 |
| |
| Typical application |
| Specifically designed to quickly repair damaged cable jacketing, providing sealing, insulation |
| and protection of odd-shaped electrical objects where tubing insulation materials are not applicable. |
| Ordering |
| Standard color : Black |
| Standard length is 1m/pc. Customized lengths (Lmax=1.5m/pc) are available. |
| Standard packaging by pieces |
| Please specify specification, customized length, quantity when ordering |
| Cross reference |
| Raychem/ Tyco : CRSM |
UPM history
In 2002, UPM was established in Dalian, China to manufacture heat shrink materials.
In 2003,UPM began selling products for shipyard and the high voltage switchgear cabinet industry.
In 2005, UPM became an approved global supplier to Siemens for High Voltage Switchgear .
In 2006, UPM began selling products to the automotive industry.
In 2007, UPM began producing heat shrink connectors, CE approved.
In 2008, UPM expanded the product line to include power cable accessories.
In 2009, UPM began producing products for the telecommunications industry.
In 2010, UPM expanded the production capability to include a variety of Moulded parts.
In 2011, UPM expanded their manufacturing expertise to include triple-layer co-extrusion products.
In 2012, UPM brought in more automated machineries used in extrusion, co-extrusion, expansion and splicing processes.
In 2013, UPM received UL486D certification for the S3(h ) and S3(nh) product lines.
In 2014, UPM began to sell triple layer tube for cable joint
In 2015, Co-extrusion tube with adhesive tube sold well.
In 2016, More products got UL 224 approval.
More news coming up... Let's shrink the world together. Let's choose Union Polymer.
Since its founding, UPM has distinguished itself with excellent product quality, comprehensive customized after-sales service, and timely delivery. Strong R&D and innovation are the core components for the sustainable growth of UPM. UPM's manufacturing plant is now 3 times larger than the original facility. The in-house 3MeV Dynamitron (3MeV E-Beam) equipment enables UPM to maintain quality control over the entire supply chain from formulation, compounding & granulation, extrusion, cross-linked radiation, expansion, adhesive application, slicing, printing, and packaging. New products are continuously being added to our product line to meet customer needs.
){kind=link}
){kind=link}