| S3PS Heat Shrink Tube for Fiber Optic Dome Closure | ||||
| Features | ||||
| Heavy wall cross-linked polyolefin | Operating temperature: -55~110ºC | |||
| Innovative locking mechanism, hermetically sealed | Shrink temperature: 125 ºC | |||
| Spiral polyamide adhesive, mirror like adhesive optional | Shrink ratio: 4:1 | |||
| Excellent UV,corrosion,mechanical damage resistance | ||||
| Thermo-chromatic paint changes color for proper installation | ||||
| Pass 10 circles of high and low temperature |
Gasoline resistant |
|||
| Dimensions | 4:1 | |||
| Reference | As supplied(mm) | After recovered(mm) | Standard length | |
| UPM S3PS | ID min. | ID max. | WT nom. | mm |
| 28/6 | 28 | 6 | 2.9 | 150 |
| 30/6 | 30 | 6 | 3.0 | 150 |
| 33/8 | 33 | 8 | 3.0 | 150 |
| 38/9 | 38 | 9 | 3.5 | 150 |
| 43/9 | 43 | 9 | 3.8 | 150 |
| 45/10 | 45 | 10 | 3.8 | 150 |
| 55/16 | 55 | 16 | 3.7 | 150 |
| 75/22 | 75 | 22 | 3.7 | 150 |
| 95/25 | 95 | 25 | 4.2 | 150 |
| 105/30 | 105 | 30 | 4.2 | 150 |
| ID=Internal Diameter | WT=wall thickness | |||
| Technical Data | ||
| Property | Test method | Values |
| Density | ASTM D2671 | 0.95~1.00 |
| Hardness (Shore D) | ASTM D2671 | ≥ 45 HD |
| Tensile strength | ASTM D2671 | ≥19 MPa |
| Breakdown elongation | ASTM D2671 | ≥450% |
| Aging Tensile strength | ASTM D2671 | ≥18 MPa |
| 158 ºC/168hrs Breakdown elongation | ASTM D2671 | ≥400% |
| Dielectric strength | ASTM D2671 | ≥15 KV/mm |
| Fungus resistance | ASTM G21 | No incidence of fungal growth |
| UV resistance | ASTM G53 | After 2000hrs elongation 360% min. |
| Water absorption | ASTM D570 | 23ºC/24hrs 0.2% max. |
| Low temperature flexibility(out layer) | ASTM D2671 | -40ºC/4hrs No cracking |
| Low temperature flexibility(adhesive layer) | ASTM D2671 | -20ºC/4hrs No cracking |
| Chemical resistance | Hydrochloric acid, concentration 0.1 | 23ºC/168hrs Elongation 400% min. |
| Sulphuric acid, concentration 0.1 | ||
| Sodium chloride,concentration 0.1 | ||
| Sodium hydroxide, concentration 0.1 | ||
| Sodium nitrate, concentration 0.1 | ||
| Sodium sulphate, concentration 0.1 | ||
| Chemical resistance | 5%HCL/5%NaOH/5%NaCl | No corrosion; No leaking |
| Internal air pressure 60kPa/24hrs | ||
| Sealing | 23ºC/100kPa duration 24hrs,or immersed in water for 15mins | Pass |
| Temperature cycling | 10 temperature cycles from -40ºC to 60ºC,internal air | No leaking |
| pressure 60kPa, duration 2hrs at each temperature point | ||
| Thermal aging | 60ºC/168hrs, internal air pressure 70kPa | Pass |
| Elongation | Pulling with D/45*1500N, internal air pressure 60kPa/24hrs | No leaking |
| Cable torsion | Subjecting the cable to 90 degree torsion loading, | No damage, No leaking |
| maximum torque:50Nm torsion distance 250mm, | ||
| internal air pressure 60kPa | ||
| Chemical attack | 70% gasoline and 30%methylbenzene | No leaking |
| duration 168hrs, after 3 days internal | ||
| air pressure 100kPa | ||
| Typical application | ||
| Ideal for aerial and underground applications, expecially in Fiber Optic Dome Splice Closure | ||
| Ordering | ||
| Standard color : Black | ||
| Special colors (e.g. Clear) are available on request | ||
| Standard packaging is 150mm/pc | ||
| Special sizes and lengths are available on request | ||
| Please specify specification,color,quantity when ordering | ||
){kind=link}